New method to determine surface properties at the nanoscale
07 April 2015
Engineering researchers at Texas Tech University have developed a method for characterising the surface properties of materials at different temperatures at the nanoscale.
“Knowing properties of materials at different temperatures is important in engineering,” said Gregory McKenna, a professor of chemical engineering at the university and the John R. Bradford Endowed Chair in Engineering. For example, the rubber O-ring that failed during the 1986 space shuttle disaster serves at a tragic case study of what can go wrong when decision-makers don’t take this into account.”
The problem, he said, is that known properties of a material can radically change at the nanoscale, which is a tiny scale about 1/1000 of the diameter of a human hair at which scientists have begun building machines that do work. McKenna and graduate student Meiyu Zhai looked at several polymers and explosive materials to see how surface properties varied at the nanoscale and how the surface impacts the nanoscale properties.
Their first results on the ‘multi-curve method’ appeared in the peer-reviewed journal, Journal of Polymer Science Part B: Polymer Physics and was highlighted in Advances in Engineering.
“The nanoscale is a funny range of sizes where materials have properties that are not what we expect, even at a step up at the microscale,” he said. “We are developing methods to characterise surface properties and relate them to nanoscale behaviour using a nanoindenter and other nano-mechanical measurement methods.”
In nanoindentation, researchers can investigate both the elastic properties (how materials spring back when pushed) and the viscous properties (how the material flows). The group has found several surprising results. For example, in other work, the team found extremely thin polycarbonate films become liquid-like at the nanoscale, while they are glassy at the macroscopic size scale. Nanoindentation can be used to relate surface properties to this observation.
As machines get smaller and smaller, McKenna said, knowing this information can be invaluable to future engineers.
Meiyu Zhai, Gregory B. McKenna. Viscoelastic modeling of nanoindentation experiments: A multicurve method. Journal of Polymer Science Part B: Polymer Physics, 2014; 52 (9): 633 DOI: 10.1002/polb.23470http://www.engineersjournal.ie/2015/04/07/new-method-determine-surface-properties-nanoscale/http://www.engineersjournal.ie/wp-content/uploads/2015/04/Nanoscale.jpghttp://www.engineersjournal.ie/wp-content/uploads/2015/04/Nanoscale-300x300.jpgChemnano,research,United States